FLOW CONTROL
Precision refractories that control molten steel, directly impacting steel quality
Flow control refractories regulate the flow of molten steel during continuous casting. They must survive extreme thermal shock, erosion from high-velocity steel, and chemical attack from steel and slag, all while maintaining dimensional tolerances critical to casting quality.
Company Profile (PDF)Industries Served
ALL PRODUCTS, FLOW CONTROL
1600°CMonoblock Stoppers
Monoblock Stoppers
Isostatically pressed alumina-graphite stopper rods for precise tundish-to-mould flow control
1600°CTundish Nozzles
Tundish Nozzles
Alumina-graphite tundish nozzles that seat the stopper and meter steel into the mould
1650°CWell Blocks
Well Blocks
High-alumina/alumina-carbon ladle bottom blocks that house the slide-gate inner nozzle
Popular 1650°CSlide Gate Plates
Slide Gate Plates
Sliding mechanism plates controlling molten steel flow from ladle to tundish
1600°CLadle Shrouds
Ladle Shrouds
Shield the steel stream from oxidation during ladle-to-tundish transfer
1600°CSubentry Nozzles (SEN)
Subentry Nozzles (SEN)
Direct steel from tundish to mould with precision flow control for surface quality
1650°CPorous Plugs & Ladle Bottom Nozzles
Porous Plugs & Ladle Bottom Nozzles
Enable argon gas stirring for steel homogenisation and inclusion flotation
NEED A RECOMMENDATION?
Our engineers specify the right grade for your operating conditions
Talk to an EngineerFLOW CONTROL REFRACTORIES, KEY PROPERTIES AT A GLANCE
Indicative property ranges across our flow control refractories portfolio. Use this table to shortlist a sub-family before reviewing the full per-grade data sheet on the product page.
| Product | Max Temp | Al₂O₃ | Carbon | Bulk Density | Specification |
|---|---|---|---|---|---|
| Slide Gate Plates | 1650°C | 85-95% | 5-12% | 3.0-3.4 g/cc | — |
| Ladle Shrouds | 1600°C | 70-85% | — | 2.8-3.2 g/cc | Anti-clogging designs |
| Subentry Nozzles (SEN) | 1600°C | 75-90% | — | — | Anti-clogging technology |
| Monoblock Stoppers | 1650°C | 80-95% | — | 3.0-3.4 g/cc | Integrated design |
| Tundish Nozzles & Well Blocks | 1600°C | 70-90% | — | — | Consistent bore design |
Values are typical ranges across stocked grades. Exact data sheets per grade and brand are available on request.
Need help choosing the right sub-family for your equipment? Talk to a refractory engineer →