Shaped Refractories / High Alumina Bricks
HA-45 High Alumina Bricks
HA-45 is the 45-50% Al₂O₃ grade in Shanker Agencies’ high alumina bricks range, rated for continuous service to 1550°C. In India it is also written AL-45 or 45% alumina. The nearest export designation is SK 35.
Also meets SK 30, SK 32, SK 34 requirements. Those are lower duties, so a lighter grade may be the more economical choice.
HA-45 technical specification
Typical values for HA-45 high alumina bricks. Test methods vary by property and product family, so confirm the applicable standard against the manufacturer datasheet before specifying.
| Property | HA-45 |
|---|---|
| Al₂O₃ content | 45-50% |
| Fe₂O₃ content | 2.5% |
| Apparent porosity | 22-26% |
| Cold crushing strength | 40 MPa |
| Refractoriness (PCE) | SK 33 |
| Max service temperature | 1550°C |
Grade designations and equivalents
How HA-45 is referenced across Indian and export naming conventions.
| SAPL grade code | HA-45 |
| Indian trade names | AL-45, 45% alumina |
| Export SK equivalentNearest SK step, minimum 45% Al₂O₃ | SK 35 |
| Also meetsExceeds these requirements, a lower grade may suit those duties | SK 30, SK 32, SK 34 |
| Alumina content | 45-50% Al₂O₃ |
| Measured refractoriness (PCE)This brick’s own cone value, not its SK trade grade | SK 33 |
| Max service temperature | 1550°C |
Reading an SK code correctly. SK (Seger Kegel) is a cone designation, and each step carries an accepted minimum Al₂O₃ content in trade practice. The dependable way to match an SK enquiry to a grade is that minimum alumina figure, which is how the equivalence above is derived. Note that a brick’s measured PCE and its SK trade grade are two different numbers and will not always agree. Suppliers also differ at the margins, most often around SK 34. When comparing offers, check Al₂O₃ and PCE together rather than the SK code alone.
SK series to high alumina bricks reference
Standard SK steps with the SAPL grade that meets or exceeds each one. Grades are matched at or above the minimum alumina for the step, so an SK enquiry is never answered with an under-spec material.
Where HA-45 is used
Full high alumina bricks range
Compare HA-45 against every grade SAPL stocks in this family.
| Grade | Al₂O₃ content | Fe₂O₃ content | Apparent porosity | Cold crushing strength | Refractoriness (PCE) | Max service temperature |
|---|---|---|---|---|---|---|
| HA-45 | 45-50% | 2.5% | 22-26% | 40 MPa | SK 33 | 1550°C |
| HA-55 | 53-57% | 2.2% | 21-25% | 45 MPa | SK 34 | 1610°C |
| HA-60 | 58-62% | 2.0% | 20-24% | 50 MPa | SK 35 | 1650°C |
| HA-70 | 68-72% | 1.8% | 18-22% | 55 MPa | SK 36 | 1750°C |
| HA-80 | 78-82% | 1.5% | 16-20% | 60 MPa | SK 37 | 1800°C |
| HA-90 | 88-92% | 1.0% | 14-18% | 70 MPa | SK 38 | 1850°C |
Installation notes
- 1Store in dry conditions, protect from moisture and contamination before use
- 2Use matching high alumina mortar (same Al₂O₃ % as brick) for jointing
- 3Maintain joint thickness 1.5–3 mm for optimal bond integrity
- 4Follow controlled dry-out schedule: 20°C/hr to 110°C, hold 12 hrs, then 30°C/hr to operating temp
- 5Apply expansion allowances: 6–8 mm per metre for silica-bonded grades, 8–10 mm for Al₂O₃ >70%
Disclaimer: values are typical and compiled by Shanker Agencies Pvt. Ltd. from standard industry data and published manufacturer specifications. They are indicative, not a guarantee. Confirm the exact grade datasheet before specifying. For a certified datasheet or quotation, contact info@shankeragencies.com or +91 98999 57888.