Unshaped Refractories / Non-Wetting Aluminium Contact Castables
High-Strength Al-Mg Resistant Non-Wetting Aluminium Contact Castables
High-Strength Al-Mg Resistant is the 79.5% Al₂O₃ grade in Shanker Agencies’ non-wetting aluminium contact castables range, rated for continuous service to 1300°C.
High-Strength Al-Mg Resistant technical specification
Typical values for High-Strength Al-Mg Resistant non-wetting aluminium contact castables. Test methods vary by property and product family, so confirm the applicable standard against the manufacturer datasheet before specifying.
Where High-Strength Al-Mg Resistant is used
Is High-Strength Al-Mg Resistant right for your application?
- Rated for continuous service up to 1300°C.
Compare High-Strength Al-Mg Resistant with other grades▾
Compare High-Strength Al-Mg Resistant against every grade SAPL stocks in this family.
Swipe to compare grades
| Grade | Al₂O₃ content | SiO₂ content | Bulk density | Cold crushing strength | Max service temperature | Application |
|---|---|---|---|---|---|---|
| Self-Flow Non-Wetting LCC | 77.2% | 11.5% | 2750 kg/m³ @110°C | 55 / 65 / 80 N/mm² @110 / 816 / 1200°C | 1300°C | Launders, holding furnace, general contact |
| High-Strength Al-Mg Resistantthis grade | 79.5% | 12% | 2800 kg/m³ @110°C | 80 / 110 / 120 N/mm² @110 / 816 / 1200°C | 1300°C | Melting furnace, Al-Mg alloys, high-impact zones |
Send the drawing, dimensions, application and quantity for High-Strength Al-Mg Resistant non-wetting aluminium contact castables. Our technical team reviews the requirement and advises on grade and fulfilment route.
Request High-Strength Al-Mg Resistant QuoteGrade designations & equivalents▾
How High-Strength Al-Mg Resistant is referenced across Indian and export naming conventions.
| SAPL grade code | High-Strength Al-Mg Resistant |
| Alumina content | 79.5% Al₂O₃ |
| Max service temperature | 1300°C |
Installation notes
- 1Self-flow grade needs approximately 6.9% water and places by self-flow or mild vibration, suited to congested launder and box shapes
- 2High-strength grade needs approximately 5–5.5% water and is vibro cast, traditional cast or pump cast
- 3Material requirement is roughly 2800 kg/m³ for the self-flow grade and 2900 kg/m³ for the high-strength grade, use these for take-off quantities
- 4Permanent linear change stays within −0.3% at 816°C and ±0.5% at 1200°C, so allow for joint movement rather than expecting zero change
- 5Dry out on a controlled schedule; trapped moisture in a dense low cement castable causes explosive spalling
- 6Never patch an aluminium contact lining with a silica-bearing material, it will be reduced by the melt
Disclaimer: values are typical and compiled by Shanker Agencies Pvt. Ltd. from standard industry data and published manufacturer specifications. They are indicative, not a guarantee. Confirm the exact grade datasheet before specifying. For a certified datasheet or quotation, contact info@shankeragencies.com or +91 98999 57888.