Shaped Refractories / Magnesia-Carbon (MgO-C) Bricks

MgO-C 14% Magnesia-Carbon (MgO-C) Bricks

MgO-C 14% is the 80-84% MgO grade in Shanker Agencies’ magnesia-carbon (mgo-c) bricks range, rated for continuous service to 1700°C.

Request MgO-C 14% QuoteCall +91 98999 57888
MgO-C 14% grade magnesia-carbon (mgo-c) bricks supplied by Shanker Agencies
Grade
MgO-C 14%
MgO content
80-84%
Carbon content
12-14%
Max service temperature
1700°C
Cold crushing strength
38 MPa

MgO-C 14% technical specification

Typical values for MgO-C 14% magnesia-carbon (mgo-c) bricks. Test methods vary by property and product family, so confirm the applicable standard against the manufacturer datasheet before specifying.

MgO content
80-84%
Carbon content
12-14%
Apparent porosity
3-6%
Cold crushing strength
38 MPa
Max service temperature
1700°C

Where MgO-C 14% is used

BOF / converter liningEAF hot spots & slag lineSteel ladle slag lineLadle metal lineAOD vessel liningConverter & EAF taphole

Is MgO-C 14% right for your application?

  • Rated for continuous service up to 1700°C.
Compare MgO-C 14% with other grades▾

Compare MgO-C 14% against every grade SAPL stocks in this family.

Swipe to compare grades

GradeMgO contentCarbon contentApparent porosityCold crushing strengthMax service temperature
MgO-C 10%86-90%8-10%4-7%40 MPa1700°C
MgO-C 14%this grade80-84%12-14%3-6%38 MPa1700°C
MgO-C 18%76-80%16-18%3-5%35 MPa1700°C
← MgO-C 10%MgO-C 18% →

Send the drawing, dimensions, application and quantity for MgO-C 14% magnesia-carbon (mgo-c) bricks. Our technical team reviews the requirement and advises on grade and fulfilment route.

Request MgO-C 14% Quote
Grade designations & equivalents▾

How MgO-C 14% is referenced across Indian and export naming conventions.

SAPL grade codeMgO-C 14%
Max service temperature1700°C

Installation notes

  1. 1Lay dry or with thin carbon-bonded mortar; keep joints tight (under 1 mm where possible)
  2. 2Match carbon level to duty: lower C for metal line, higher C (16–18%) for slag line
  3. 3Limit oxidising atmosphere during heat-up to protect the carbon bond
  4. 4Antioxidant-containing grades develop a dense protective zone in service

Disclaimer: values are typical and compiled by Shanker Agencies Pvt. Ltd. from standard industry data and published manufacturer specifications. They are indicative, not a guarantee. Confirm the exact grade datasheet before specifying. For a certified datasheet or quotation, contact info@shankeragencies.com or +91 98999 57888.