Alumina-Zr-C (2QC) Well Blocks
Alumina-Zr-C (2QC) is the 78-85% Al₂O₃ grade in Shanker Agencies’ well blocks range, rated for continuous service to 1650°C.
Alumina-Zr-C (2QC) technical specification
Typical values for Alumina-Zr-C (2QC) well blocks. Test methods vary by property and product family, so confirm the applicable standard against the manufacturer datasheet before specifying.
| Property | Alumina-Zr-C (2QC) |
|---|---|
| Al₂O₃ content | 78-85% |
| Apparent porosity | 8-12% |
| Cold crushing strength | 70 MPa |
| Bulk density | 3.0 g/cc |
| Max service temperature | 1650°C |
Grade designations and equivalents
How Alumina-Zr-C (2QC) is referenced across Indian and export naming conventions.
| SAPL grade code | Alumina-Zr-C (2QC) |
| Alumina content | 78-85% Al₂O₃ |
| Max service temperature | 1650°C |
Where Alumina-Zr-C (2QC) is used
Full well blocks range
Compare Alumina-Zr-C (2QC) against every grade SAPL stocks in this family.
| Grade | Al₂O₃ content | Apparent porosity | Cold crushing strength | Bulk density | Max service temperature |
|---|---|---|---|---|---|
| Alumina-C (1QC) | 80-85% | 10-14% | 60 MPa | 2.9 g/cc | 1600°C |
| Alumina-Zr-C (2QC) | 78-85% | 8-12% | 70 MPa | 3.0 g/cc | 1650°C |
| Mag-Sp-C (3QC) | 70-80% | 9-14% | 65 MPa | 3.0 g/cc | 1650°C |
Installation notes
- 1Set into the ladle bottom with matching ramming/bedding mass; ensure concentric nozzle seating
- 2Align with the slide-gate mechanism before securing
- 3Controlled dry-out with the ladle lining; protect carbon-bearing grades from oxidation
- 4Match grade (Al₂O₃-C / Zr-C / Mag-Sp-C) to steel grade and campaign target
Disclaimer: values are typical and compiled by Shanker Agencies Pvt. Ltd. from standard industry data and published manufacturer specifications. They are indicative, not a guarantee. Confirm the exact grade datasheet before specifying. For a certified datasheet or quotation, contact info@shankeragencies.com or +91 98999 57888.