Unshaped Refractories / Low Cement Castables

LCC-85 Low Cement Castables

LCC-85 is the 83-87% Al₂O₃ grade in Shanker Agencies’ low cement castables range, rated for continuous service to 1800°C.

Also known asLCC-8585% alumina

Request LCC-85 Quote Call +91 98999 57888

Grade

LCC-85

Al₂O₃ content

83-87%

Max service temperature

1800°C

CCS after 110°C dry

70 MPa

Bulk density

3.00 g/cc

LCC-85 technical specification

Typical values for LCC-85 low cement castables. Test methods vary by property and product family, so confirm the applicable standard against the manufacturer datasheet before specifying.

Al₂O₃ content

83-87%

Cement content

2-3%

Bulk density

3.00 g/cc

CCS after 110°C dry

70 MPa

CCS after 1200°C

140 MPa

Max service temperature

1800°C

Where LCC-85 is used

Steel ladle barrel, cone, and bottomTundish working liningTorpedo car barrel liningReheating furnace hearth & skid pipesHot metal mixer liningBlast furnace cast house runners

Is LCC-85 right for your application?

Rated for continuous service up to 1800°C.

Compare LCC-85 with other grades▾

Compare LCC-85 against every grade SAPL stocks in this family.

Swipe to compare grades

Grade	Al₂O₃ content	Cement content	Bulk density	CCS after 110°C dry	CCS after 1200°C	Max service temperature
LCC-60	58-62%	4-5%	2.60 g/cc	40 MPa	80 MPa	1650°C
LCC-70	68-72%	3-4%	2.70 g/cc	50 MPa	100 MPa	1700°C
LCC-80	78-82%	3-4%	2.90 g/cc	60 MPa	120 MPa	1750°C
LCC-85this grade	83-87%	2-3%	3.00 g/cc	70 MPa	140 MPa	1800°C

← LCC-80

Send the drawing, dimensions, application and quantity for LCC-85 low cement castables. Our technical team reviews the requirement and advises on grade and fulfilment route.

Request LCC-85 Quote

Grade designations & equivalents▾

How LCC-85 is referenced across Indian and export naming conventions.

SAPL grade code	LCC-85
Indian trade names	85% alumina
Alumina content	83-87% Al₂O₃
Max service temperature	1800°C

Installation notes

1Pre-wet forms and ensure they are leak-proof before casting
2Mix with measured water (4.5–5.5%) in a pan mixer for 5–8 minutes to achieve flow
3Cast in layers no thicker than 300 mm and vibrate thoroughly to eliminate voids
4Cover with polythene sheet after casting to retain moisture during curing (24 hrs minimum)
5Critical dry-out: 25°C→110°C at 20°C/hr, hold 12 hrs; 110°C→300°C at 15°C/hr, hold 8 hrs; then 30°C/hr to operating temperature
6Never accelerate dry-out with open flame, steam explosion risk

Disclaimer: values are typical and compiled by Shanker Agencies Pvt. Ltd. from standard industry data and published manufacturer specifications. They are indicative, not a guarantee. Confirm the exact grade datasheet before specifying. For a certified datasheet or quotation, contact info@shankeragencies.com or +91 98999 57888.